Qhov txawv ntawm Composite Cladding thiab Dual Cladding
Composite txheej yog hais txog kev tso tawm ib txhij ntawm ob lossis ntau dua txheej txheej ntawm TiO2 hais nyob rau hauv tib lub acidic lossis alkaline. Dual txheej yog hais txog kev tso tawm ntawm ntau tshaj ib tus neeg sawv cev hauv ib qho xwm txheej thiab tom qab ntawd qhov kev tso tawm ntawm ntau tshaj ib tus neeg txheej txheej thib ob hauv qhov no lossis lwm qhov xwm txheej.
Cov txheej txheem txheej txheem txheej txheem sib xyaw yog raws li hauv qab no: cov dej slurry uas muaj 300g / L TiO2 thiab pH =9 ~ 11 yog ntxiv rau hauv lub tank kho, thiab ob kwj ntawm cov kua qaub thiab alkaline tau qhia tib lub sijhawm nyob rau hauv zoo nplawm. Acid flow content (g/L): 50MgS04, 100TiOSO4, 50H2SO4; Alkaline kua dej (g / L): 100Na2SiO3, 75NaAlO2. Qhov piv thiab tus nqi sib ntxiv ua rau cov slurry ib txwm nyob nruab nrab ntawm pH 6 ~ 8.
Binary txheej yog ib txoj kev siv ntau, thiab saum toj no-hais deposition ntawm ntom SiO2 nyob rau hauv alkaline tej yam kev mob thiab ces deposition ntawm Al2O3 nyob rau hauv acidic tej yam kev mob yog ib tug raug bivariant txheej. Kev txhim kho tsis ntev los no yog thawj zaug tso ib lub hnab ntawv ntom ntom ntawm SiO2 thiab Al2O3 nyob rau hauv alkaline tej yam kev mob (pH=11), thiab tom qab ntawd kho cov pH txog li 3 rau acid stabilization rau 15-30 min (ntev dhau rau> 1h yuav ua rau thawj lub hnab ntawv tawg). Tom qab ntawd, pH ntawm cov slurry tau nce mus rau 5 ~ 5.5, thiab thawj binary txheej tau ua nrog Al2O3, uas txhim kho cov dispersion thiab optical zog ntawm TiO2.